ICS87.060.99 CCSJ31 团 体 标 准 T/CFA0202063—2023 消失模壳型铸造用涂料 Coatingsforlostfoamshellmoldcasting 2023-08-25发布 2023-11-25实施 中国铸造协会  发布 全国团体标准信息平台 全国团体标准信息平台 T/CFA0202063—2023 I 目次 前 言............................................................................II 引 言...........................................................................III 1范围.................................................................................1 2规范性引用文件.......................................................................1 3术语和定义...........................................................................1 4分类和牌号...........................................................................1 5技术要求.............................................................................2 6试验方法.............................................................................3 7检验规则.............................................................................4 8标志、包装、运输和贮存...............................................................5 附录A（规范性）消失模壳型铸造用涂料性能试验方法........................................6 图A.1涂层抗弯强度测定装置示意图....................................................7 图A.2涂层透气性测定试样筒示意图....................................................8 表1涂料按耐火粉料分类...............................................................2 表2面层涂料性能指标.................................................................2 表3背层涂料性能指标.................................................................3 表4消失模壳型铸造用涂料检验要求.....................................................4 全国团体标准信息平台 T/CFA0202063—2023 II 前言 本文件按照GB/T1.1—2020《标准化工作导则第1部分：标准化文件的结构和起草规则》的规定 起草。 请注意本文件的某些内容可能涉及专利。本文件的发布机构不承担识别专利的责任。 本文件由中国铸造协会消失模V法实型铸造分会提出。 本文件由中国铸造协会归口。 本文件起草单位：河南天缘精工模具股份有限公司、河南天聚缘新材料科技有限公司、河北科技大 学、芜湖泓鹄材料技术有限公司、山西华恩实业有限公司、衡水中裕铁信装备工程有限公司、郑州翔宇 铸造材料有限公司。 本文件主要起草人：张守军，李立新，李云飞，徐达义，张国华，郭勇，朱翔，张洪富，于凯伦。 本文件为首次发布。 全国团体标准信息平台